| Tensile test (speed 4 mm/min) with cladding segment of rod #01: two ruptures at hydrogen bands above and below the burst. Movie acceleration x16 until rupture, then slowing factor 16. The pobe is marked with white circumference rings. |
| Tensile test (speed 2 mm/min) with cladding segment of rod #9: contraction and rupture at upper holder. Movie acceleration x64. The probe is marked with white cicumference rings. |
|
Tensile test (speed 4 mm/min) with cladding segment of rod #12: rupture at burst middle. Movie acceleration x32. The porbe is marked with white cirumference rings. |